O objetivo do trabalho foi avaliar a resistência natural de chapas de partículas orientadas (OSB)
confeccionadas com partículas de Hevea brasiliensis Müll.Arg. aderidas com as resinas sintéticas uréia-
formaldeído (UF) e fenol-formaldeído (FF), a 5% e 8%, expostas a fungos xilófagos em condições de
laboratório. No ensaio acelerado de laboratório as amostras foram submetidas ao ataque dos fungos de
podridão-parda Gloeophyllum trabeum (Pers. : Fr.) Murril, Coniophora puteana (Schumach. : Fr.) P. Karst.,
Meruliporia incrassata (Berk. & M.A. Curtis) Murrill e também aos fungos de podridão-branca, Fomes
annosus (Fr. : Fr.) Cooke, Trametes versicolor (L. : Fr.) Pilát, Ganoderma applanatum (Pers.) Pat.,
Bjerkandera fumosa (Pers. : Fr.) P. Karst. e Phanerochaete chrysosporium Burds. Dentre os fungos de
podridão-parda, o Gloeophyllum trabeum causou a maior perda de massa nos corpos-de-prova testados.
Dentre os fungos de podridão-branca, Trametes versicolor, Phanerochaete chrysosporium e Ganoderma
applanatum causaram as maiores perdas de massa, sem diferença significativa para o Gloeophyllum trabeum.
A resina FF proporcionou maior resistência à ação dos fungos nas chapas OSB, o mesmo fato ocorrendo com
o maior teor de resina. O fungo Coniophora puteana foi altamente sensível ao tipo de resina aplicado,
enquanto o Bjerkandera fumosa demonstrou reduzida ação nas concentrações mais altas de ambas as resinas.
O fungo Fomes annosus apresentou degradação insignificante para todos os tratamentos de chapas OSB.
This work aimed to evaluate the natural durability of oriented strandboards (OSB) manufactured
with strands of Hevea brasiliensis Müll.Arg. bonded with 5% and 8% of urea-formaldehyde (UF) and
phenol-formadehyde (FF) resins, exposed to xilophagous fungi under laboratory conditions. In accelerated
laboratory test decay, samples of OSB were exposed to the following fungi: the brown-rot fungi
Gloeophyllum trabeum (Pers. ex Fries) Murr., Coniophora puteana (Schumach. : Fr.)P. Karst., Meruliporia
incrassata (Berk. & M.A. Curtis) Murrill as well as the white-rot fungi Fomes annosus (Fr. : Fr.) Cooke,
Trametes versicolor (L. : Fr.) Pilát, Ganoderma applanatum (Pers.) Pat., Bjerkandera fumosa (Pers. : Fr.) P.
Karst. and Phanerochaete chrysosporium Burds. Among the brown-rot fungi, the Gloeophyllum trabeum
was the most aggressive, showing the highest loss of mass. Trametes versicolor and Ganoderma applanatum
confirmed the preference for broadleave species. All oriented strandboards at lower UF resin contents were
more degraded by Phanerochaete chrysosporium, Trametes versicolor, Ganoderma applanatum, Merulia
incrassata, Coniophora puteana and Gloeophyllum trabeum, with high rate of loss of mass. Coniophora
puteana showed small loss of mass when FF resin was applied. Bjerkandera fumosa showed low loss of
mass only at higher resin content. Oriented strandboards exposed to Coniophora puteana showed insignificant OSB degradation.