O objetivo desta pesquisa foi avaliar a corrosão de parafusos auto-rosqueáveis fixados à madeira tratada com soluções preservativas preparadas com creosoto vegetal, em condições de campo. Obteve-se o creosoto vegetal bruto por meio da destilação à temperatura de 110 – 255oC do alcatrão vegetal. Uma fração dos destilados foi lavada com solução a 9% de bicarbonato de sódio, obtendo-se o creosoto vegetal purificado. Ambas as frações foram enriquecidas com 3% de naftenato de cobre; 3% de naftenato de zinco; 3% naftenato de cobalto; 2% de TBTO; 2% de tribromofenato de tubutil-estanho; 2% de pentaclorofenol; ou 0,4% de trióxido de arsênico. Foram preparadas 16 soluções, sendo 14 enriquecidas, além do creosoto vegetal bruto e do creosoto vegetal purificado. Estacas confeccionadas com madeira de alburno de Eucalyptus grandis foram tratadas pelo processo de célula- cheia (processo Bethell). Após o tratamento, parafusos auto-rosquéaveis de ferro zincado foram fixados às estacas. O ensaio foi instalado em três localidades da Zona da Mata de Minas Gerais (Viçosa, Ponte Nova e Leopoldina). A corrosividade das soluções de creosoto vegetal foi comparada à causada pelo creosoto mineral. As soluções preparadas com creosoto vegetal purificado foram menos corrosivas que suas similares preparadas com creosoto vegetal bruto, assemelhando-se ao creosoto mineral.
The objective of this research was to evaluate the corrosion of screws fixed into wood treated with preservative solutions of wood tar creosote. The crude wood tar creosote was obtained through distillation of wood tar at 110 - 255oC. A fraction of this product was washed with a solution of sodium bicarbonate at 9%, resulting in purified wood tar creosote. Both fractions were enriched with 3% of copper naphtenate, 3% of zinc naphtenate, 3% of cobalt naphtenate, 2% of TBTO, 2% of tributhyl-tin tribromophenate, 2% of pentachlorophenol, or with 0.4% of arsenic trioxide. A total of 16 preservative solutions were prepared, of which 14 were enriched, besides the crude wood tar creosote and the purified wood tar creosote. Stakes made of Eucalyptus grandis sapwood were treated following the full-cell process (Bethell’s process). After the stakes treatment, screws of iron covered with zinc were fixed into the wood stakes. The assay was carried out in three locations (Viçosa, Ponte Nova and Leopoldina - in Zona da Mata, Minas Gerais, Brazil). The corrosiveness of solutions of wood tar creosote was compared with the one caused by coal tar creosote. The solutions with purified wood tar creosote were less corrosive than those prepared with crude wood tar creosote, being similar to the coal tar creosote.