Chapa aglomerada de cimento-madeira de Hevea brasiliensis Müll. Arg.

Mostrar registro simples

dc.contributor.author Okino, Esmeralda Yoshico Arakaki
dc.contributor.author Souza, Mário Rabelo de
dc.contributor.author Santana, Marcos Antonio Eduardo
dc.contributor.author Sousa, Maria Eliete de
dc.contributor.author Teixeira, Divino Eterno
dc.date.accessioned 2014-11-25T11:05:51Z
dc.date.available 2014-11-25T11:05:51Z
dc.date.issued 2004
dc.identifier.citation OKINO, E. Y. A. et al. Chapa aglomerada de cimento-madeira de Hevea brasiliensis Müll. Arg. Revista Árvore, Viçosa, v. 28, n. 3, p. 451-457, 2004. pt_BR
dc.identifier.issn 1806-9088
dc.identifier.uri http://www.bibliotecaflorestal.ufv.br/handle/123456789/12932
dc.description.abstract Chapas de partículas de cimento-madeira foram confeccionadas com a madeira de quatro clones de Hevea brasiliensis Müll. Arg. (seringueira): IAN 717, IAN 873, GT 711 e AVROS 1301. Confeccionaramse as chapas na proporção de 1:4:1 (madeira:cimento:água) por peso e nas dimensões de 450 x 450 x 13 mm e densidade nominal de 1,4 g/cm³, com a adição de 4% de cloreto de cálcio di-hidratado (CaCl2.2H2O) como acelerador. Foram testadas partículas fervidas e não-fervidas dos quatro clones, totalizando oito tratamentos, sendo em cada um destes, com quatro repetições, avaliadas as propriedades mecânicas e físicas das chapas, segundo a norma ASTM D 1037 – 96a. De forma geral, os melhores resultados de propriedades físicas e mecânicas foram obtidos nas chapas com partículas do clone AVROS 1301. No teste de hidratação do cimento, a madeira de seringueira in natura foi classificada como de “inibição extrema”, porém com a adição de CaCl2 o foi como de “baixa inibição”. Essa madeira se mostrou tecnicamente viável à produção de chapas de cimento-madeira, independentemente do clone. pt_BR
dc.description.abstract Cement-bonded particleboards of rubberwood were manufactured with four clones of Hevea brasiliensis Müll. Arg. (rubberwood): IAN 717, IAN 873, GT 711 and AVROS 1301. Boards of 450 x 450 x 13 mm were manufactured in a ratio of 1:4:1 (wood/cement/water), weight basis, with 1.4 g/cm3 density and 4% calcium chloride dihydrated - CaCl2.2H2O as accelerator. The particles of four clones were tested in treated and untreated conditions, totaling eight treatments. In each treatment with four replicates, the physical and mechanical properties were evaluated according to ASTM D 1037 - 96a standard. Overall, the best mechanical and physical results were obtained with the cement-bonded particleboard made with particles from clone AVROS 1301. Rubberwood has shown to be “highly inhibitory” in the hydration test, however when CaCl2 was added the inhibition index decreased and was classified as “low inhibitory”. Rubberwood is technically feasible to make cement-bonded particleboard. pt_BR
dc.format 7 páginas pt_BR
dc.language.iso pt_BR pt_BR
dc.publisher Sociedade de Investigações Florestais pt_BR
dc.relation.ispartofseries Revista Árvore;v.28,n.3
dc.subject.classification Ciências Florestais::Tecnologia e utilização de produtos florestais::Tecnologia de chapas pt_BR
dc.title Chapa aglomerada de cimento-madeira de Hevea brasiliensis Müll. Arg. pt_BR
dc.title Cement-bonded particleboard of Hevea brasiliensis Müll. Arg. pt_BR
dc.type Artigo pt_BR

Arquivos deste item

Arquivos Tamanho Formato Visualização
Revista_Arvore_v28_n3_p451-457_2004.pdf 84.33Kb application/pdf Visualizar/Abrir ou Pre-visualizar

Este item aparece na(s) seguinte(s) coleção(s)

Mostrar registro simples

Buscar em toda a Biblioteca


Sobre a Biblioteca Florestal

Navegar

Minha conta