The objetive of this work was to estimate the rigidity and strenght properties of plywood manufactured of Pinus elliottii Engelm with venner and wood strength properties. The results of theoric calculations of modulus of elasticity (MOE) and modulus of rupture (MOR) of plywood in the parallel and perpendicular directions had a strong equivalence with the values observed through convencional tests. The best estimated value to the MOE parallel was 7,6% higher than the value observed and 0,4% lesser than perpendicular MOE. MOR was 0,5% lesser on parallel direction and 5% lesser on perpendicular direction. The theoric estimate mechanical properties of plywood on parallel directions, considering only the parallel venner of span, was of 1,2% and 18% lesser on MOE parallel and perpendicular in relation to the value obtained using all transversal section and 1,4% and 9,8% lesser in the case of MOR.
Este trabalho teve como objetivo estimar as propriedades de resistência e de rigidez de compensados de Pinus elliottii Engelm, a partir das propriedades de resistência tanto da madeira sólida como lâminas. Os resultados dos cálculos teóricos do módulo de elasticidade (MOE) e do módulo de ruptura (MOR) dos compensados nas direções paralela e perpendicular, tiveram uma forte equivalência aos valores observados através de ensaios convencionais. O melhor valor estimado para o MOE no sentido paralelo foi 7,6% maior que o valor observado, e de 0,4% menor para o MOE no sentido perpendicular. Para o MOR foi de 0,5% menor no sentido paralelo e de 5% menor no sentido perpendicular. As propriedades mecânicas dos compensados no sentido paralelo estimadas teoricamente, considerando atuantes somente as lâminas sob tensão paralelas ao vão, foram de 1,2% e 18% menor para MOE paralelo e perpendicular em relação ao calculado considerando toda a seção, e de 1,4% e 9,8% menor no caso do MOR.