O presente trabalho teve por objetivo avaliar a resistência de chapas de partículas orientadas - OSB (oriented strandboard), confeccionadas com as resinas uréia-formaldeído (UF) e fenol-formaldeído (FF) a 5% e a 8% de sólidos resinosos (baseado no peso seco das partículas) e strands de Pinus taeda L., Eucalyptus grandis W Hill ex Maiden e Cupressus glauca Lam. Para o teste de degradação acelerada foram usados os fungos de podridão-parda Gloeophyllum trabeum (Persoon ex Fries) Murr. e Lentinus lepideus Fries e os fungos de podridão-branca Trametes versicolor (Linnaeus ex Fries) Pilat. e Ganoderma applanatum (Persoon ex Wallroth) Patouillard. A determinação da classe de resistência ao apodrecimento foi feita por meio da porcentagem de perda de massa. Todas as chapas orientadas apresentaram maior perda de massa quando expostas ao fungo G. trabeum, com exceção das chapas orientadas de eucalipto. No geral, o incremento no teor de resina UF tornou as chapas menos suscetíveis ao ataque dos fungos. De forma geral, o fungo L. lepideus apresentou o menor ataque e o G. trabeum o maior. Quanto à espécie, chapas com strands de eucalipto sofreram o menor ataque e as de pinus o maior. Com relação à resina, painéis de FF em nível de 8% apresentaram maior resistência ao ataque de fungos.
The objective of this work was to evaluate the fungi susceptibility of several oriented strandboards - OSB using urea-formaldehyde (UF) and phenol-formaldehyde (FF) resins at 5% and 8% of solids contents (based on the ovendry weight of particles) and wood strands of Pinus taeda L., Eucalyptus grandis W Hill ex Maiden and Cupressus glauca Lam. In accelerated bioassay it was used four rotters, two brown-rot fungi, Gloeophyllum trabeum (Persoon ex Fries) Murr., Lentinus lepideus Fries and two white-rot fungi, Trametes versicolor (Linnaeus ex Fries) Pilat. and Ganoderma applanatum (Persoon ex Wallroth) Patouillard. The decay resistance class was based upon percentage of the mass loss. Among all studied fungi, the G. trabeum showed the highest mass loss to all treatments, except to the eucalyptus oriented strandboards. In general, an increment in UF resin content led to increase in the durability of the panels. In general, the panels of eucalyptus were the least attacked by the fungi. On the other hand, panels of pine were the most attacked. Regarding to fungi type, the order of decay, from the least to the most severe, was L. lepideus (4.42%), T. versicolor (10.99%), G. applanatum (12.86%), and G. trabeum (20.45%). Panels with 8% FF resin were less attacked by the rotters.