This study performed a behavioral analysis of different structural composition boards constructions utilizing taeda Pine Venner in the core. Two densities (0,60 and 0, 75 g/cmª) and two resin levels (6 and 8%) were used totalizing 12 treatments. The constmctions with 1 and 2 vencers in the core were compared in their properties to composition boards with no veneer and five ply plywood. The following properties were studied linear expansion, thickness swelling, modulus of elasticity, and internal bond. The results demonstrated that the two ply vencer core eficiently reduces linear expansion and thickness swelling. Modulus of elasticity is not affected by the inclusion of vencer, and the internal bond values are lower than those for no veneer in the core. Composition boards with veneer core can be an economical alternative for industry.
Este trabalho fez uma análise comportamental de 2 construções diferentes de chapas de partículas estruturais utilizando no seu miolo lâminas de madeira de Pinus taeda. Foram utilizadas duas densidades nominais (0,60 e 0, 75 g/cm3) e duas percentagens de adesivo (6 e 8%). As construções com 1 e 2 lâminas foram comparadas com chapas sem lâmina e compensado de 5 camadas. As propriedades analisadas foram, expansão linear, inchamento em espessura, módulo de elasticidade e ligação interna. Os resultados demonstraram que a inclusão de dupla camada de lâminas realmente se traduz na redução da expansão linear e inchamento em espessura. Módulo de elasticidade é praticamente não afetado pela inclusão laminar, e os valores de ligação interna caem. A conclusão e que a inclusão laminar pode ser uma alternativa industrial econômica.